Tribotechnical characteristics of gas-thermic spraying coating with different types of hardening
DOI:
https://doi.org/10.18372/2306-1472.1.10988Abstract
The triboengineering characteristics of gas-thermal spraying coating with different types of hardening in friction in respect to bronze have been examined. It has been established that high level of it corresponds to formation of heterogeneous secondary structures of the mixed type on the coatings. The coatings, based on Ni, after intermetallide hardening have better properties than coatings based on Fe-Ni, containing the phases of penetration MeCReferences
Ригни Д. Процессы изнашивания при трении скольжения // Трение и износ, 1987.-Т. 8. № 6 - С. 973 - 976.
Костецкий Б.И., Бергиадский Л.И. Динамическое равновесие при трении и доносе металлов//ДАН СССР, 1970,-Т. 191. №6,-С. 2337 - 1339.
Методы анализа структур поверхностей, формирующихся в процессе трения/ H.H. Кузьмин, Е.А. Шувалова, Г.Р. Транковская Г.Р. и др.// Трение и износ, 1996.-Т. 17-№ 4- С. 480 - 486.
Костецкая Н.Б. Механизмы деформирования и разрушения поверхностей трения при трибоокислительных процессах // Сверхтвердые материалы, 1986 - №1. - С. 48 - 54.
Горский В.В. Формирование легированных кислородом сплавов Ме-Мег-0 в зоне контакта металлов при трении// Трение и износ, 1989,- Т. 10 - № 3,- С. 452 - 460.
Современные жаростойкие материалы. Справочник /Под ред С.Б. Масленкова. М.: Металлургия, 1986. - 359 с.
Кириенко О.Ф. Структурно-масштабная модель безызносного трения металлических конструкционных материалов в условиях структурной самоорганизации // Трение и износ, 1993. -Т.143. -№1, - С. 85-97.