Deformation relief in the area of fatigue crack
DOI:
https://doi.org/10.18372/2306-1472.32.1475Abstract
Results of observation of the alclad aluminium alloy surface state near fatigue crack are presented. It is shown, that deformation relief near stress concentrator expresses fatigue damage of the material not only at the initial stage of fatigue, but at the fatigue crack propagation stage as well. The damage parameter D, that determines the intensity of the surface micro plastic deformation features can be considered as quantitative parameter of fatigue crack propagation rate.
References
Карускевич О.М., Игнатович С.Р., Карускевич М.В., Пантелеев В.М. Диагностика усталости плакированных алюминиевых сплавов // Вестн. НТТУ “КПИ”. Машиностроение. – 2002. – №43. – С. 53–55.
Моніторинг утоми конструкційних алюмінієвих сплавів / О.М. Карускевич, С.Р. Ігнатович, М.В. Карускевич та ін. // Вісн. НАУ. – 2004. – № 1(19). – С. 88–91.
Karuskevich M.V. Aircraft life prediction by the parameters of foil sensors and skin surface // Вестн. двигателестроения. – 2006. – № 3. – С. 88–92.
Карускевич О.М., Игнатович С.Р., Карускевич М.В. Эволюция поврежденности сплава Д-16АТ у концентратора на стадии до зарождения усталостной трещины // Науч.-техн. журн. Нац. аэрокосмического ун-та им. Н.Е. Жуковского «ХАИ». Авиационно-космичес-кая техника и технология. – 2004. – № 4(12). – С. 29–32.